Accuracy of Intraoral Scanners: A Systematic Review of Influencing Factors

Abstract

To evaluate fracture resistance of occlusal veneers made of glass-ceramic and zirconia with and without fatigue. Occlusal overlays (N=80; n=10 per group) were milled out of CAD/CAM materials, namely: a)LD:Lithium disilicate glass ceramic, b)LDS:Lithium-disilicate-strengthened aluminosilicate glass ceramic, c)ZLT:Zirconium dioxide ceramic and d)ZMT:Zirconium dioxide ceramic. The overlays were cemented on polymeric duplicates, randomly distributed to aging or non-aging conditions and loaded until fracture. Ultimate catastrophic failure strength(Fmax) and Initial crack formation load(Finitial) values were analysed using two-way ANOVA. For Finitial, material type and aging and their interaction resulted in significant values (p =<0.001). Finitial mean±SD values ranged from ZMTa (593 N ±205 N) to LDSb (118 N ±42 N). As for Fmax, the material type significantly affected the outcome (p<0.001), while aging type did not show an influence (p=0.795). The non-aged Fmax specimens values presented were: LDSa (877 N ±253 N)<LDa (2029 N ±412 N)<ZLTa (2049 N ±379 N)<ZMTa (2144 N ±333 N), LDSa being significantly lower (p<0.001). The aged Fmax values were: LDSb (1313 N ±599 N)< ZLTb (1715 N ±453 N)<ZMTb (2018 N ±300 N)<LDb (2134 N ±289 N). LDS yielded significantly lower Fmax values without and non-significant less favourable results with aging. The mechanical properties following aging and lack of additional firing makes LDS an interesting restorative material for clinical application.
Keywords
Zirconia
CAD/CAM
Lithium Disilicate
Fracture Resistance
Mechanical Loading
Occlusal Veneers

Authors

Dr. Jaafar Abduo, Dr. Mohamed Elseyoufi

Articles from this issue

Title / DOI Access Page Start Page End Purchase
Accuracy of Intraoral Scanners: A Systematic Review of Influencing Factors
10.1922/EJPRD_01752Abduo21
no access 101 121 £10.00
Effect of Bioactive Composites on Microhardness of Enamel Exposed to Carious Challenge
10.1922/EJPRD_01781Pinto07
no access 122 128 £10.00
Comparative Evaluation of Surface Defects In Single File Rotary Systems Before and After Instrumentation In Curved Root Canals
10.1922/EJPRD_01714Purayil06
no access 130 135 £10.00
Effect of Zirconia Pigmentation on Translucency
10.1922/EJPRD_01779Gomes07
no access 136 142 £10.00
The Effect of Try-In Paste and Resin Cement Shade on Colour Properties of Dental Veneers
10.1922/EJPRD_01768Alghazali08
no access 144 151 £10.00
Clinical Evaluation of Sonic Activated High Viscosity Bulk-Fill Nanohybrid Resin Composite Restorations in Class II Cavities: A Prospective Clinical Study up to 2 Years
10.1922/EJPRD_01620Akalin09
no access 152 160 £10.00
  • free access Free Access
  • no access No Access
  • full access Full Access

Subscriptions